ADD-ON AND GLAZE
This shade-matching flowable Add-on is light cure and is formulated from the same proprietary rubberized-resin chemistry. It is ideal for making alterations and for smile design.
The light cure glaze has the same proprietary rubberized-resin chemistry that provides enhanced esthetics and patient satisfaction during temporization.
FLEXURAL STRENGTH
Tuff-Temp Plus exhibits very high flexural strength without brittleness. Its deflection at break, the key indicator of toughness, is 50% to 100% greater than bis-acrylics.
Deflection at Break (mm)
Tuff-Temp Plus
0 0.5 1.0 1.5 2.0
Protemp, Luxatemp and ProSpan are not trademarks Pulpdent.
PHYSICAL PROPERTIES
Working time:
Light cure setting time: Initial self-cure setting time: Final self-cure setting time: Flexural strength: Compressive strength: Deflection at break: Vickers Hardness:
2.5 3.0
20 seconds 2 minutes from beginning of mix 4:45 minutes from beginning of mix 75 (+/- 5) MPa 200 (+/- 20) MPa 2.9 mm (+/- 0.3 mm) 514 MPa
45 seconds
TTP*
50mL (76 gm) cartridge, 1.2mL Add-on, and 3mL Glaze + 20 Automix tips + 6 tips *Specify shade: A1, A2, A3, A3.5, B, B1
TTP5*
5mL (7.6 gm) and 3mL Glaze + 8 Automix tips
* Specify shade: A1, A2, A3, A3.5, B, B1
TTP50*
50mL (76 gm) cartridge, + 10 Automix tips
* Specify shade: A1, A2, A3 only
TTG
Bottle of 6mL glaze
FSB20
20 Automix tips for 50mL cartridge
A20
20 Automix tips for 5mL syringe
DS50
Dispenser for 50mL, 1:1 Automix cartridge
1
Fill matrix 3⁄4 full with Tuff-Temp Plus and seat in the mouth.
2
Removal time is 2 minutes from the beginning of the mix (approximately 75 seconds after insertion in the mouth).
3
Check the provisional restoration for marginal integrity.
4
The provisional is trimmed and polished but not yet glazed. Note the perfect margins.
5
The 12-unit provisional is glazed and cemented to place. The margins and esthetics are exceptional
6
Note the excellent tissue condition upon removal of the provisional four weeks later.
Photography courtesy of Dr. Christopher Ramsey